Knife number 2
« on: March 10, 2013, 10:07:42 pm »
I made this today -



It is 1080 carbon steel that I heat treated and tempered myself (first time doing it) The blade is 3.75" and the handle is 3.5". I just drew a shape and went with it...





Logged
>>>---------->

Offline Frawg

  • Member
  • Posts: 282
  • Mayan Apocalypse Survivor
    • N/A
Re: Knife number 2
« Reply #1 on: March 10, 2013, 10:51:43 pm »
Very nice Duck, I really like that one great job.
Matt
Logged
Matt Bradley

Glade Valley, NC

Offline Olanigw (Pekane)

  • Member
  • Posts: 488
Re: Knife number 2
« Reply #2 on: March 10, 2013, 11:17:39 pm »
Nice beefy knife.
Logged
"Good enough" is the enemy of great
PN501018

Offline osage outlaw

  • Member
  • Posts: 11,962
Re: Knife number 2
« Reply #3 on: March 10, 2013, 11:34:48 pm »
I like it.
Logged
I started out with nothin' and I still got most of it left

Offline Pappy

  • Global Moderator
  • Member
  • Posts: 32,198
  • if you have to ask you wouldn't understand ,Tenn.
Re: Knife number 2
« Reply #4 on: March 11, 2013, 09:09:38 am »
I like it,very nice work.  :)
   Pappy
Logged
Clarksville,Tennessee
TwinOaks Bowhunters
Life is Good

Offline Cardboard_Duck

  • Member
  • Posts: 282
  • Winter Haven, FL
Re: Knife number 2
« Reply #5 on: March 11, 2013, 09:08:17 pm »
Thanks for the comments :)

I brought it to work today, showed the guys at my shop and got some good constructive criticism. Some liked the weight of the 1/8" thick blade, some didn't, they also said the handle was a bit small. Overall good I guess.

I also abused the #$%@ out of it  >:D first a put a good edge on it with a Work Sharp knife sharpener and cut everything I could with it  >:D  >:D  >:D even some 6065 aluminum!! I have to say it held an edge even after the aluminum shaving session, but I'm assuming I didn't have a high enough or long enough heat session for the temper so it must be brittle... but I knew that when my files wouldn't touch it after the tempering. All part of the learning process right :)
Logged
>>>---------->