How bad is it?
« on: October 10, 2012, 11:39:48 pm »
Was applying heat to a section of limb to make a slight correction and my attention wandered.  The back is now lightly "toasted".



How bad is this?  I can probably sand off most of the dis-colored wood, but I am very concerned that I have now lost this osage's strength in tension on this spot.  I do not have enough wood to take off the growthring, either. 

I'm thinking scrape down this spot to plain yellow, back it with high quality rawhide and tiller with all fingers crossed. 

Oh, and the other marks on the wood are sawdust and pencil marks, not nicks/scratches/grain violations or the like. 
Logged
Guns have triggers. Bicycles have wheels. Trees and bows have wooden limbs.

Offline coaster500

  • Member
  • Posts: 1,741
Re: How bad is it?
« Reply #1 on: October 11, 2012, 12:46:46 am »
I've done that a couple of times JW...  so far it hasn't been a problem???

That really doesn't look that bad ...
Logged
Inspiration, information and instruction by the ton and it's free,,, such a deal :)

Offline k-hat

  • Member
  • Posts: 1,058
Re: How bad is it?
« Reply #2 on: October 11, 2012, 01:05:35 am »
Had that happen too, did what you're saying w/o problems.  What do you have to lose?  Slap some hide on'r and go with it ;)
Logged

Offline sleek

  • Member
  • Posts: 6,764
Re: How bad is it?
« Reply #3 on: October 11, 2012, 01:09:14 am »
I wouldnt use rawhide. Not because the stuff doesnt work, but I really dont think you need it. If you can just scrape lightly and get that off, it didnt go too deep. Also, where in the bend will that spot be? You can alter the limb profile and the therefore the tiller to control the stresses on that area as well. Lots of ways around this problem, which I think is small.
Logged
Tread softly and carry a bent stick.

Dont seek your happiness through the approval of others

Offline osage outlaw

  • Member
  • Posts: 11,962
Re: How bad is it?
« Reply #4 on: October 11, 2012, 01:28:18 am »
JW, did a pretty girl walk by?  ;D
Logged
I started out with nothin' and I still got most of it left

Offline Cameroo

  • Member
  • Posts: 1,579
    • Cam's Stuff
Re: How bad is it?
« Reply #5 on: October 11, 2012, 01:34:02 am »
His mind probably just drifted for a while as he dreamt about smoking little piggies :)
Logged

Offline Hrothgar

  • Member
  • Posts: 1,477
Re: How bad is it?
« Reply #6 on: October 11, 2012, 09:54:08 am »
JW, I don't think thats a problem, I would sand it a little and go on. I've used osage before that was a victim of a 'forest fire' and it worked fine.
Logged
" To be, or not to be"...decisions, decisions, decisions.

Offline bluegill68

  • Member
  • Posts: 140
Re: How bad is it?
« Reply #7 on: October 11, 2012, 11:37:33 am »
JW,

I have done similar toasting both accidental and purposely. That Osage is so clean, I would not worry about backing. How thick are your growth rings?

The only issue you will face is cosmetic.

Sean
Logged

Offline Gordon

  • Member
  • Posts: 3,299
Re: How bad is it?
« Reply #8 on: October 11, 2012, 11:57:40 am »
I don't think that will be a problem.
Logged
Gordon

Offline BowEd

  • Member
  • Posts: 9,390
  • BowEd
Re: How bad is it?
« Reply #9 on: October 11, 2012, 12:07:14 pm »
Diddo.It'll be OK.Anybody who has worked with hedge long enough has done this a time or two.Me included.Show us your triumph when you finish the bow.
Logged
BowEd
You got to stand for something or you'll fall for anything.
Ed

Offline Will H

  • Member
  • Posts: 2,120
Re: How bad is it?
« Reply #10 on: October 11, 2012, 01:11:03 pm »
I agree, it's not an issue
Logged
Proud Member of Twin Oaks Bowhunters
           Clarksville, Tennessee